C95400 Aluminum Bronze Plate
C95400(CuAl10Fe) Aluminum bronze is the most common cast aluminum bronze, C95400 is used in many heavy duty, high load and high wear applications. Good tensile strength, ductility, weldability and resistance to fatigue. Typical applications include worm gears, bushings, pump parts and bearings.
Product Description
| Bronze Plate & Sheet - Product Specification Table | ||
| Property Category | Specification | Description / Typical Values |
| General Information | Common Names | Bronze Plate, Bronze Sheet, Bronze Shate (Distinguished by thickness) |
| Material Standards | ASTM B103, ASTM B122, ASTM B171, CDA 95400, CDA 95500, CDA 90300 | |
| Material Composition | Primary Alloys | Aluminum Bronze (e.g., C95400), Tin Bronze (e.g., C90300), Nickel-Aluminum Bronze (e.g., C95500) |
| Key Elements | Cu (Copper), Al (Aluminum), Sn (Tin), Ni (Nickel), Fe (Iron) | |
| Physical Properties | Density | Approximately 8.78 - 8.94 g/cm³ (Varies by alloy) |
| Melting Point | ~ 1040 - 1065 °C (1900 - 1950 °F) | |
| Thermal Conductivity | 40 - 80 W/m·K | |
| Mechanical Properties | Tensile Strength | 450 - 960 MPa (65,000 - 140,000 psi) |
| Yield Strength (0.2% Offset) | 170 - 550 MPa (25,000 - 80,000 psi) | |
| Elongation (% in 2") | 12% - 45% | |
| Hardness | 80 - 200+ Brinell (HB) (High-strength aluminum bronzes are hardest) | |
| Key Characteristics | Corrosion Resistance | Exceptional, especially against seawater, acids, and wear. |
| Wear & Galling Resistance | Excellent (A primary reason for selection) | |
| Machinability | Fair to Good (20% - 80% of free-cutting brass) | |
| Non-Sparking | Yes (Critical for tools in explosive environments) | |
| High Strength | Retains strength at elevated temperatures. | |
| Available Forms | Thickness Classification | Sheet: Typically < 3.0 mm (0.125") Plate: Typically > 3.0 mm (0.125") |
| Thickness Range | 0.5 mm - 150 mm (0.020" - 6 inches) and thicker | |
| Width & Length | Standard sheets/plates or cut-to-size. | |
| Temper | Annealed, As-Rolled, Hard | |
| Common Applications | Industrial | Wear Plates, Bushings, Gears, Thrust Bearings, Valve Components |
| Marine & Offshore | Propellers, Hull Fittings, Pump Components, Deck Hardware | |
| Architectural | Decorative Facades, Sculptures, Roofing | |
| Specialized Tools | Non-Sparking Tools for Oil & Gas, Mining, and Chemical Industries | |
| Alloy / UNS Designation | Thickness Range | Standard Sheet/Plate Size | Temper / Condition | Key Properties |
| C93200 / SAE 660 - High Leaded Tin Bronze | Sheet: 0.032" - 0.500" (0.81mm - 12.7mm) Plate: 0.500" - 3" (12.7mm - 76.2mm) Casting Stock: Available | 24" x 48" (610mm x 1219mm) 36" x 96" (914mm x 2438mm) Custom cast sizes | As Cast Annealed Stress Relieved | Excellent Bearing Properties Good Machinability (70%) Low Friction Coefficient High Load Capacity |
| C95400 - Aluminum Bronze (9% Al) | Plate: 0.250" - 6" (6.35mm - 152.4mm) Sheet: 0.063" - 0.249" (1.6mm - 6.3mm) | 48" x 96" (1219mm x 2438mm) 60" x 120" (1524mm x 3048mm) Custom cut pieces | Annealed Heat Treated As Rolled | High Strength: 90 ksi Yield Excellent Corrosion & Erosion Resistance Good Wear Resistance Non-Sparking |
| C63000 - Nickel Aluminum Bronze (AMS 4590) | Plate: 0.500" - 8" (12.7mm - 203.2mm) Sheet: 0.125" - 0.499" (3.18mm - 12.7mm) | 48" x 120" (1219mm x 3048mm) 72" x 144" (1829mm x 3658mm) Custom forged/rolled | Solution Treated & Aged Annealed Hot Rolled | Very High Strength: 110 ksi Tensile Excellent Fatigue Resistance Superior Corrosion Resistance High Temperature Stability |
| C51000 - Phosphor Bronze (5% Sn) | Sheet: 0.006" - 0.250" (0.15mm - 6.35mm) Shim Stock: 0.001" - 0.005" (0.025mm - 0.13mm) | 24" x 48" (610mm x 1219mm) 36" x 96" (914mm x 2438mm) Coils up to 24" width | Annealed (O61) Quarter Hard (H02) Half Hard (H04) Hard (H08) Spring Temper | Excellent Spring Properties Good Fatigue Resistance High Elastic Limit Good Formability |
| C90500 - Gun Metal (88-10-2) | Plate: 0.500" - 4" (12.7mm - 101.6mm) Casting Plate: Custom thickness | Custom cast sizes only Machined to specification | As Cast Annealed | Excellent Pressure Tightness Good Corrosion Resistance Machinability: 40% Historical Casting Alloy |
| C17200 - Beryllium Copper | Plate: 0.125" - 2" (3.18mm - 50.8mm) Sheet: 0.010" - 0.124" (0.25mm - 3.15mm) | 24" x 48" (610mm x 1219mm) 36" x 48" (914mm x 1219mm) Custom sizes available | Solution Annealed (AT) Mill Hardened (HT) Solution Treated & Aged | Very High Strength: 200 ksi Excellent Conductivity: 22% IACS Non-Sparking Good Wear Resistance |