C44300 Admirality Brass Plate
Brass is a copper alloy with zinc and a small amount of other alloying such as Arsenic adding which can inhibit the corrosion and improve the corrosion resistance. Alloy C44300 also known as admiralty brass and has good mechanical properties. Brass C44300 of lkalloy supplying is available in tubing and sheet. C44300 brass tubing offers excellent cold workability for forming and bending, ideal for heat exchangers and pipes that transporting corrosive liquids.
Product Description
| Brass Plates - Detailed Technical Specifications | ||||
| Common Brass Plate Grades and Classifications | ||||
| UNS No. | Common Name | Nominal Copper (%) | Nominal Zinc (%) | Key Characteristics |
| C21000 | Gilding Brass, 95% | 95 | 5 | Highest copper content; excellent corrosion resistance; warm golden color; good formability |
| C22000 | Commercial Bronze, 90% | 90 | 10 | Good corrosion resistance; good formability; CZ101 / H90 grade available |
| C22600 | Jewelry Bronze, 87.5% | 87.5 | 12.5 | Good formability; attractive appearance |
| C23000 | Red Brass, 85% | 85 | 15 | Good corrosion resistance; good cold working properties |
| C24000 | Low Brass, 80% | 80 | 20 | Good cold working properties; higher zinc content than red brass |
| C26000 | Cartridge Brass, 70% | 70 | 30 | Excellent cold working properties; high ductility; most common brass alloy; exceptional cold workability; high strength-to-ductility ratio |
| C26800 | Yellow Brass, 66% | 66 | 34 | Good strength; good corrosion resistance |
| C27200 | 63/37 Brass | 63 | 37 | Good ductility and corrosion resistance |
| C28000 | Muntz Metal, 60% | 60 | 40 | Good corrosion resistance; high strength; good ductility; good machinability; good weldability; excellent formability |
| Mechanical Properties - UNS C26000 (Cartridge Brass) Plate | ||||
| Condition | Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) | Hardness (HV) |
| Annealed (O) | 300 – 400 | 100 – 150 | 55 – 70 | 50 – 70 |
| Cold Worked (H02 - Half Hard) | 450 – 550 | 350 – 420 | 15 – 25 | 100 – 130 |
| Cold Worked (H04 - Full Hard) | 550 – 650 | 480 – 550 | 5 – 12 | 140 – 180 |
| Mechanical Properties - UNS C37700 Brass Plate | ||||
| Condition | Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) | Hardness (HV) |
| Annealed (O) | 260 – 440 | 100 – 200 | 35 – 50 | 75 – 100 |
| Cold Worked (H02 - Half Hard) | 450 – 550 | 350 – 450 | 15 – 25 | 120 – 160 |
| Hard (H04 - Full Hard) | ≥ 550 | ≥ 450 | ≥ 5 | ≥ 160 |